Name: Industrial Mold Slag
Diagram No.: 967
Type of diagram: TTT
Chemical composition in weight %: 37.8% CaO, 33.3% SiO2, 7.9% Al2O3, 8.2% Na2O, 8.4% T.F., 0.6% MgO, 0.6% K2O, 1.7% Fe2O3
Group: Slags
Note: TTT diagram of industrial mold slag obtained.
The diagram was divided into two regions above and below 1050 C as two distinct curves were detected which suggested two separate nucleation events. Each of the curves in the TTT diagram had a C-shape and the observed crystal morphology drastically changedat 1050 C.
The minimum time before the crystalline phase could be determined was approximately lOs at 1070 C and 950 C. The critical cooling rates for glass formation would be 30 C/s or higher for this industrial mold slag. The necessity of considering crystallization as function of time and temperature is clearly seen in Fig. Also clear from this figure is that there is no specific crystallization temperature for a mold flux but a range of temperatures defined by experimental conditions.
Reference: Not shown in this demo version.

Transformation Diagram

Price: 30.00 US $
Buy Online Transformation Diagram

Other Steel Data links
Carbides in Steel
Etchants Database
Hardenability Diagrams of Steels
Macro Defects in Steel
Non-Metallic Inclusions in Steel
Tempering Diagrams of Steels
CCT and TTT Diagram Calculating Service
Transformation Diagrams of Non-Ferrous Alloys

Disclaimer: The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.

Copyright © 2019 by Steel Data. All Rights Reserved.