0.4C-0.65Mn-0.08Al-V-Cr Steel

0.4C-0.65Mn-0.08Al-V-Cr Steel

Steel name: 0.4C-0.65Mn-0.08Al-V-Cr
Diagram No.: 4924
Type of diagram: CCT
Chemical composition in weight %: See the table.
Steel group: Abrasion resistant steels
Note: Austenitizing temperature: 1100 C. In the Gleeble, the specimens were heated to 1100°C at 20°C/s, held at temperature for 4 min and then cooled at 2°C/s. When no deformation was applied, cooling was stopped at 1000°C where the specimens were held for 2 min. In the case of deformed austenite, cooling was stopped at 850°C for 10 s for compressive deformation.
Links: No. 4922, No. 4923, No. 4924, No. 4925 and No. 4926.
Reference: Esko Kinnunen, et al., Development of a New Direct Quenched Abrasion Resistant Steel, International Journal of Metallurgical Engineering 2013, 2(1): 27-34.

Transformation Diagram

Click the image to enlarge the diagram.

Disclaimer: The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.